Product Description
This product is a laminated sheet which made with processed non-alkali glass fiber cloth as the backing material, by hot pressing with grade F benzo oxazine resin. It has good mechanical and electrical properties,and flame retardant, especially has high mechanical strength retention and excellent electrical properties under high temperature.Suitable for grade F motor and electrical equipment as high quality insulation structure , has the advantage of good machinability and wide applicability in the similar products.
Features
1.Good mechanical and electrical properties;
2.High mechanical strength retention and excellent electrical properties under high temperature;
3.Moisture resistance;
4.Heat resistance;
5.Temperature resistance:Class F,155℃
6.Good Machinability and wide applicability
7.Flame retardant property:UL94 V-0
Compliance With Standards
In accordance with GB/T 1303.4-2009 electrical thermosetting resin industrial hard laminates – Part 4: epoxy resin hard laminates.
Appareance: the surface should be flat, free of bubbles, pits and wrinkles, but other defects that do not affect the use are allowed, such as: scratches, indentation, stains and a few spots.The edge shall be cut neatly, and the end face shall not be delaminated and cracked.
Application
The technical data of 347F is similar to FR5,Suitable for grade F motor and electrical equipment as high quality insulation structure.
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | |||
| 01 | Density | g/cm³ | 1.8-2.1 | |||
| 02 | Water absorption | % | <0.5 | |||
| 03 | Vertical bending strength | Normal | MPa | ≥400 | ||
| 155±2℃ | ≥250 | |||||
| 04 | Impact strength（Charpy type） | No Gap | Lengthways | KJ/m² | ≥129 | |
| Lateral | ≥77 | |||||
| 05 | compression strength | Vertical | MPa | ≥300 | ||
| Parallel | ≥200 | |||||
| 06 | Tensile strength | Lenthways | MPa | ≥240 | ||
| Lateral | ≥180 | |||||
| 07 | Bond strength | N | ≥6800 | |||
| 08 | Vertical electric strength（in oil of 90℃±2℃ 1min） | 1mm | MV/m | ≥14.2 | ||
| 2mm | ||||||
| ≥12.4 | ||||||
| 3mm | ||||||
| ≥11.5 | ||||||
| 09 | Parallel breakdown voltage（in oil of 90℃±2℃） | KV | ≥45 | |||
| 10 | Relative dielectric constant（50Hz) | - | ≤5.5 | |||
| 11 | dielectric dissipation factor（50Hz) | - | ≤0.04 | |||
| 12 | Parallel insulation resistance | Normal | MΩ | ≥1.0×106 | ||
| After soaking for 24 hours | ≥1.0×104 | |||||
| 13 | Surface/volumn insulation resistance | Normal | MΩ | ≥1.0×106 | ||
| After soaking for 24 hours | ≥1.0×104 | |||||
| 155±2℃ | ≥1.0×104 | |||||
| Fire retardant(UL-94) | V-0 | |||||
Product detail pictures:
Related Product Guide:
In an effort to provide you advantage and enlarge our business enterprise, we even have inspectors in QC Staff and assure you our greatest provider and item for Manufacturing Companies for Fiber Glass Board - 347F High Strength Epoxy Glassfiber laminated sheet (Thermostability is grade F) – Xinxing, The product will supply to all over the world, such as: Albania, Monaco, Russia, We have top engineers in these industries and an efficient team in the research. What is more, we have our own archives mouths and markets in China at low cost. Therefore, we can meet different inquiries from different clients. Please find our website to check more information from our products.
By Edwina from London - 2018.11.04 10:32
As an international trading company, we have numerous partners, but about your company, I just want to say, you are really good, wide range, good quality, reasonable prices, warm and thoughtful service, advanced technology and equipment and workers have professional training, feedback and product update is timely, in short, this is a very pleasant cooperation, and we look forward to the next cooperation!
By Caroline from Ottawa - 2017.07.07 13:00