High definition Flexible Fiberglass Sheets - 347F High Strength Epoxy Glassfiber laminated sheet (Thermostability is grade F) – Xinxing
High definition Flexible Fiberglass Sheets - 347F High Strength Epoxy Glassfiber laminated sheet (Thermostability is grade F) – Xinxing Detail:
Product Description
This product is a laminated sheet which made with processed non-alkali glass fiber cloth as the backing material, by hot pressing with grade F benzo oxazine resin. It has good mechanical and electrical properties,and flame retardant, especially has high mechanical strength retention and excellent electrical properties under high temperature.Suitable for grade F motor and electrical equipment as high quality insulation structure , has the advantage of good machinability and wide applicability in the similar products.
Features
1.Good mechanical and electrical properties;
2.High mechanical strength retention and excellent electrical properties under high temperature;
3.Moisture resistance;
4.Heat resistance;
5.Temperature resistance:Class F,155℃
6.Good Machinability and wide applicability
7.Flame retardant property:UL94 V-0
Compliance With Standards
In accordance with GB/T 1303.4-2009 electrical thermosetting resin industrial hard laminates – Part 4: epoxy resin hard laminates.
Appareance: the surface should be flat, free of bubbles, pits and wrinkles, but other defects that do not affect the use are allowed, such as: scratches, indentation, stains and a few spots.The edge shall be cut neatly, and the end face shall not be delaminated and cracked.
Application
The technical data of 347F is similar to FR5,Suitable for grade F motor and electrical equipment as high quality insulation structure.
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | |||
| 01 | Density | g/cm³ | 1.8-2.1 | |||
| 02 | Water absorption | % | <0.5 | |||
| 03 | Vertical bending strength | Normal | MPa | ≥400 | ||
| 155±2℃ | ≥250 | |||||
| 04 | Impact strength（Charpy type） | No Gap | Lengthways | KJ/m² | ≥129 | |
| Lateral | ≥77 | |||||
| 05 | compression strength | Vertical | MPa | ≥300 | ||
| Parallel | ≥200 | |||||
| 06 | Tensile strength | Lenthways | MPa | ≥240 | ||
| Lateral | ≥180 | |||||
| 07 | Bond strength | N | ≥6800 | |||
| 08 | Vertical electric strength（in oil of 90℃±2℃ 1min） | 1mm | MV/m | ≥14.2 | ||
| 2mm | ||||||
| ≥12.4 | ||||||
| 3mm | ||||||
| ≥11.5 | ||||||
| 09 | Parallel breakdown voltage（in oil of 90℃±2℃） | KV | ≥45 | |||
| 10 | Relative dielectric constant（50Hz) | - | ≤5.5 | |||
| 11 | dielectric dissipation factor（50Hz) | - | ≤0.04 | |||
| 12 | Parallel insulation resistance | Normal | MΩ | ≥1.0×106 | ||
| After soaking for 24 hours | ≥1.0×104 | |||||
| 13 | Surface/volumn insulation resistance | Normal | MΩ | ≥1.0×106 | ||
| After soaking for 24 hours | ≥1.0×104 | |||||
| 155±2℃ | ≥1.0×104 | |||||
| Fire retardant(UL-94) | V-0 | |||||
Product detail pictures:
Related Product Guide:
The organization upholds the philosophy of "Be No.1 in good quality, be rooted on credit history and trustworthiness for growth", will keep on to provide previous and new customers from home and overseas whole-heatedly for High definition Flexible Fiberglass Sheets - 347F High Strength Epoxy Glassfiber laminated sheet (Thermostability is grade F) – Xinxing, The product will supply to all over the world, such as: South Korea, Panama, Iceland, Many years of work experience, we have now realized the importance of providing good quality products and solutions and the best before-sales and after-sales services. Most problems between suppliers and clients are due to poor communication. Culturally, suppliers can be reluctant to question things they do not understand. We break down those barriers to ensure you get what you want to the level you expect, when you want it. faster delivery time and the product you want is our Criterion .
By Maria from Liberia - 2018.11.11 19:52
Wide range, good quality, reasonable prices and good service, advanced equipment, excellent talents and continuously strengthened technology forces，a nice business partner.
By Danny from Costa Rica - 2018.06.03 10:17