Factory wholesale Fiberglass Reinforced Plastic Board - 3233 Melamine Glassfiber Lamiated Sheet – Xinxing
Factory wholesale Fiberglass Reinforced Plastic Board - 3233 Melamine Glassfiber Lamiated Sheet – Xinxing Detail:
Product Description
This product is a laminated sheet which is made of eletrical alkali free glass cloth impregnated with melamine resine by hot pressing.
Features
1.Good arc resistance properties;
2.Good dielectric properties ;
3.High Mechanical strength
4.Flame resistance:UL 94 V-0
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | ||
| 01 | Density | g/cm³ | 1.8-2.0 | ||
| 02 | Water absorption | % | ≤2 | ||
| 03 | Vertical bending strength | MPa | ≥200 | ||
| 05 | Parallel impact strength（Charpy type） | KJ/m² | ≥25 | ||
| 07 | Vertical electric strength（in oil of 90℃±2℃） | 1mm | MV/m | ≥7.0 | |
| 2mm | |||||
| ≥5.4 | |||||
| 3mm | |||||
| ≥5.0 | |||||
| 08 | Parallel breakdown voltage（in oil of 90℃±2℃） | KV | ≥15 | ||
| 09 | Comparative creepage tracking index | - | ≥500 | ||
| 10 | Arc resistance | S | 180 | ||
| 11 | Insulation resistance | Normal | Ω | ≥5.0×1010 | |
| After soaking for 24 hours | |||||
| ≥5.0×10 | |||||
| Fire resistance | - | FV0 | |||
Product detail pictures:
Related Product Guide:
"Based on domestic market and expand overseas business" is our development strategy for Factory wholesale Fiberglass Reinforced Plastic Board - 3233 Melamine Glassfiber Lamiated Sheet – Xinxing, The product will supply to all over the world, such as: Australia, Spain, Niger, We focus on providing service for our clients as a key element in strengthening our long-term relationships. Our continual availability of high grade products in combination with our excellent pre-sale and after-sales service ensures strong competitiveness in an increasingly globalized market.
By Jean Ascher from UAE - 2017.11.20 15:58
We are a small company that has just started, but we get the company leader's attention and gave us a lot of help. Hope we can make progress together!
By Louis from Slovakia - 2017.06.16 18:23