Discountable price High Voltage Insulation Materials - 3240 Halogen-free fire retardant Epoxy phenolic glass fiber laminated sheet – Xinxing
Discountable price High Voltage Insulation Materials - 3240 Halogen-free fire retardant Epoxy phenolic glass fiber laminated sheet – Xinxing Detail:
Product Description
3240 Halogen-free fire retardant Epoxy phenolic glass fiber laminated sheet:This product is a laminated product made of electrical purposed alkali-free glass cloth impregnated with epoxy phenolic resin by hot pressing.The thermostablity is grade B.It has good mechanical and dielectrical properties,Applicable to mechanical, electrical, electronic, electrical and other fields. It is also used in the processing of insulating parts, and processed into all kinds of insulating parts and equipment insulating structural parts, which can be used in wet environment conditions and transformer oil.
The more important is this 3240 laminate is Halogen-free and fire retardant,which is eco-friendly and can be acceptable by European and American markets.
Compliance with standards:
In accordance with GB/T 1303.4-2009 electrical thermosetting resin industrial hard laminates – Part 4: epoxy resin hard laminates, IEC 60893-3-2-2011 insulating materials – electrical thermosetting resin industrial hard laminates – Part 3-2 of the individual material specification EPGC201.
Features
1.Good mechanical properties;
2.Good dielectrical properties;
3.Moisture resistance,suitable under
wet environment and transformer oil.
4.Good machinability properties
5.Temperature resistance:Grade B
6.Halogen-free and fire retardant
Application:
1) Used in the mechanical performance requirements of a high motor, electrical equipment and insulating struct ral parts
2) ICT,ITE rule the processing of the insulation parts,test fixtures,silicon rubber keypads mold
3) Fixture plate , mold plywood,countertops grinding plate,packaging machines,comb,etc
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | ||
| 1 | Density | g/cm³ | 1.8-2.0 | ||
| 2 | Water absorption Rate | % | ≤0.5 | ||
| 3 | Vertical bending strength | MPa | ≥340 | ||
| 4 | Vertical compression strength | MPa | ≥350 | ||
| 5 | Parallel impact strength (charpy type-gap) | KJ/m² | ≥33 | ||
| 6 | Parallel impact strength (cantilever beam method) | KJ/m² | ≥34 | ||
| 7 | Parallel shear strength | Mpa | ≥30 | ||
| 8 | Tensile strength | MPa | ≥200 | ||
| 9 | Vertical electric strength （in oil of 90℃±2℃） |
1mm | KV/mm | ≥14.2 | |
| 2mm | ≥11.8 | ||||
| 3mm | ≥10.2 | ||||
| 10 | Parallel breakdown voltage(in oil of 90℃±2℃） | KV | ≥35 | ||
| 11 | Dielectric dissiption factor（50Hz) | - | ≤0.04 | ||
| 12 | Insulation Resistance | Normal | Ω | ≥5.0×1012 | |
| After soaking for 24hours | ≥5.0×1010 | ||||
| 13 | Combustibility（UL-94) | Level | V-0 | ||
Product detail pictures:
Related Product Guide:
We thinks what clients think, the urgency of urgency to act from the interests of a purchaser position of principle, allowing for greater top quality, decrease processing costs, price ranges are much more reasonable, won the new and aged prospects the support and affirmation for Discountable price High Voltage Insulation Materials - 3240 Halogen-free fire retardant Epoxy phenolic glass fiber laminated sheet – Xinxing, The product will supply to all over the world, such as: Mexico, Ecuador, moldova, With a fully integrated operation system, our company has won a good fame for our high quality products, reasonable prices and good services. Meanwhile, we have established a strict quality management system conducted in material incoming, processing and delivery. Abiding by the principle of "Credit first and customer supremacy", we sincerely welcome clients from home and abroad to cooperate with us and advance together to create a brilliant future.
By Astrid from Jamaica - 2018.12.10 19:03
This company has the idea of "better quality, lower processing costs, prices are more reasonable", so they have competitive product quality and price, that's the main reason we chose to cooperate.
By Klemen Hrovat from Paraguay - 2018.06.12 16:22